Atmospheric glow plasma polymerization was applied to wood powder before fabricating polypropylene (PP) matrix composites. Seven different types of monomers (Oxygen, Benzene, CH4, Acrylic-acid, Hexafluoroethane, Trifluorotolune, Hexamethyl-disiloxane) were analyzed to determine the most suitable precursor for plasma polymerization. The surface energy was calculated from measured contact angle about each monomer on PP. Hexamethyl-disiloxane (HMDSO) had a highest surface energy and is selected as the most suitable monomer. Wood powder and polypropylene were mixed as pellets by twin screw extruder and then 50 wt% wood powder/PP composites were produced by an injection machine. Tensile strength and Flexural strength have improved by 7.59% and 12.43% at the maximum respectively. SEM (Scanning Electron Microscope) observation on the fracture surface revealed that the plasma polymerization have improved the interfacial bonding and the mechanical properties of the composites.

상온·상압 플라즈마 표면처리된 목분을 폴리프로필렌(polypropylene)과 혼합하였을 때 두 재료의 계면에 미치는 영향을 연구하였다. 목분과 폴리프로필렌을 압출기를 통해 기계적으로 혼합한 후 사출기를 이용하여 목 분함유량 50 wt% 목분/폴리프로필렌(Wood Plastic Composite, WPC) 복합재를 제조하였다. 플라즈마 표면처리 공 정에 가장 적합한 Monomer(모노머)를 찾기 위해 Oxygen, Benzene, CH-4, Acrylic-acid, Hexafluoroethane, Trifluorotolune, Hexamethyl-disiloxane(HMDSO) 등 7가지의 모노머에 대해 Contact angle(접촉각)을 측정하여 표면에너지를 계산 하였다. 그 결과 HMDSO가 가장 높은 표면에너지를 나타내어 플라즈마 공정의 모노머로 적용하였다. 소수성인 폴리프로필렌과 친수성인 목분을 플라즈마 표면처리를 통하여 목분의 표면을 개질하였고 두 재료의 계면 결합력 을 향상시킬 수 있었다. 기계적 물성평가 결과는 인장강도의 경우 최대 7.59%, 굴곡강도의 경우 최대 12.43%가 증 가하였다. SEM(Scanning Electron Microscope)을 이용하여 파단면을 관찰하였고 플라즈마 표면처리의 효과를 확인하였다.

Keywords: plasma, wood plastic composite, wood powder, Hexamethlydisiloxane

Keywords: 플라즈마, WPC, 목분, 핵사메틸디시록세인