  • Fabrication and Evaluation of Wear Properties of CF/GNP Composites
  • S. J. Kim*, S. B. Park*, C. H. Huh**, J. I. Song*†
  • *Department of Mechanical Engineering, Changwon National University *†Department of Mechanical Engineering, Changwon National University, Corresponding author (E-mail: jisong@changwon.ac.kr) **Department of Energy and Mechanical Engineering, Gyeongsang National University
  • Graphene Nanoplatelets을 첨가한 탄소직조복합재료의 제조 및 마모 특성 평가
  • 김상진* · 박승빈* · 허선철** · 송정일*†
Abstract
ABSTRACT: CNT and GNP have several excellent mechanical properties including, high strength, Young's modulus,thermal conductivity, corrosion resistance, electronic shielding and so on. In this study, CF/CNT, GNP/epoxycomposites were manufactured by varying the CNT weight ratio at 2wt% and 3wt%, GNP weight ratio at 0.5wt%and 1 wt%. The composites were manufactured by mechanical method (3-roll-mill). Tensile, impact and wear testswere performed according to ASTM standards D638, D256 and D3181 respectively. The results showed that, CF/GNP0.5 wt%/epoxy composites gave good mechanical property in all composites, e.g., tensile strength, impact andwere resistance.

초 록: CNT 및 GNP는 고강도, 고강성, 열전도율, 내부식성, 전자 차폐성 등 여러 우수한 기계적 특성을 갖기 때 문에, 우주 항공분야, 전자기기 소재 및 에너지 소재에 사용되고, 제동 시 흡수 에너지가 크고 안정된 제동 효과 를 나타내기 때문에 경주용 자동차나 항공기의 브레이크 디스크 재료로도 각광받고 있다. 본 연구에서는 CNT 중량비를 2 wt% 및 3 wt%, GNP 중량비를 0.5 wt%, 1 wt% 변화시켜 CF/CNT, GNP/Epoxy 복합재료를 제조하였다. 복 합 재료는 기계적 방법(3-롤밀)에 의해 제조되었다. 기계적 특성은 인장, 충격 및 마모 테스트를 각각 ASTM D638, D256과 D3181에 따라 수행하였다. 시험 결과 CF/GNP0.5 wt%/Epoxy 복합재료가 인장, 충격, 마모시험에서 우수 한 특성을 보였다.

Keywords: Epoxy resin, CNT, GNP, 3-roll-mill, Wear Property

Keywords: 에폭시, 탄소 나노튜브, 그래핀 나노플레이트렛, 3-롤밀, 마모 특 성