  • Effect of Moisture Absorption on the Fiber-reinforced Composite Materials
  • Yun-Hae Kim , Kook-Jin Kim , Young-Dae Jo , Sung-Youl Bae , Kyoung-Man Moon , Joong-Won Han**, and Dong-Hun Kim
  • 섬유강화 복합재료의 전단강도에 미치는 흡습의 영향
  • 김윤해(한국해양대학교 기계소재공학부), 김국진(한국해양대학교 대학원), 조영대(한국해양대학교 대학원), 배성열(한국해양대학교 대학원), 문경만(한국해양대학교 기계소재공학부), 한중원(한국해양대학교 기계소재공학부), 김동훈(한국해양대학교 기계소재공학부)
Abstract
Composite materials are currently used in aero-space industry, sport and leisure industry but it has many problems such as mechanical properties deterioration by moisture absorption. In this study, we appraised interlaminar shear strength with specimen that immersed/ immersed - dried in water environment(distilled/sea) during 100~200days. In the result, properties degradation of resin part and silan part by moisture absorption is judged early on main cause of interlaminar shear strength, and later destruction of mechanical bonding between silan part and fiber by moisture absorption is judged later main cause of interlaminar shear strength. In conclusion, the recovery of interlaminar shear strength is judged to difficult due to interfacial destruction by moisture when pass over irreversible by moisture in composite material.

복합재료는 현재 항공-우주산업, 스포츠 와 레저 산업에서 널리 사용되고 있으나, 흡습에 의해 기계적 성질이 저하하는 문제점을 가지고 있다. 본 연구에서는 이러한 문제점에 대한 규명을 위해 80℃의 수 환경(담수/해수)에서 100~200일 동안 침지/침지 - 건조한 시편으로 전단강도를 평가하였다. 그 결과, 전단강도의 하락은 초기에는 수지부의 흡습과 실란부의 흡습에 의한 물성저하 그리고 나중에는 실란부와 섬유와의 기계적 결합의 파괴가 주요원인으로 판단되었다. 결론적으로, 복합재료 내의 수분으로 인해 비가역구간을 넘어서게 되면 수분으로 인한 계면 파괴가 일어나 전단강도 회복이 어려워지는 것으로 판단된다.

Keywords: (Interlaminar Shear Strength(ILSS), Moisture Absorption Ratio, Cross-linked Structure, Process of Moisture Absorption

Keywords: 계면전단강도, 흡습율, 가교결합, 흡습과정