Graphene flakes are generally mass-produced by converting graphene oxide into reduced graphene oxide using chemical or thermal reduction. These graphene flakes can be stacked to form a free-standing graphene paper, which can be used for various applications. However, a graphene paper lacks stretchability, which hinders its application in stretchable devices. In this work, we introduced wrinkles in a graphene paper to make it stretchable. A graphene paper fabricated by vacuum-filtering a graphene dispersion was placed on a pre-stretched adhesive film. When the pre-stretched adhesive film returned to the original state, the graphene paper was wrinkled. The effect of the pre-stretching and wet condition of the graphene papers was experimentally investigated by using scanning electron microscopy. In addition, we observed the change of the period of the wrinkles in the graphene paper depending on the pre-stretching.

일반적으로 그래핀 플레이크는 산화그래핀을 화학적 또는 열적 환원 공정을 통해 환원그래핀으로 변환하여 대량 생산하고 있다. 그래핀 플레이크는 다양한 형태로 응용되는데, 그 중 진공여과를 이용한 적층 공정을 통해 종이형 필름으로 제작이 가능하다. 그래핀 종이는 신축성이 부족한 단점이 있어 신축성 소자 응용에 제약이 있다. 본 연구에서는 신축성이 있는 그래핀 종이를 제작하기 위하여, 그래핀 종이에 주름을 만들었다. 신축성이 뛰어난 접착 필름을 미리 늘린 후, 그 위에 그래핀 종이를 붙이고, 접착 필름을 원래 상태로 놓아 주어 그래핀 종이에 주름을 만들었다. 이 때, 접착 필름에 가하는 당김 정도 및 젖은 상태에 따라 주름의 형상이 변하는 것을 실험적으로 관찰하였다. 특히, 그래핀 종이와 접착 필름의 전단 탄성 계수 차에 의하여 주름의 주기가 바뀌는 현상을 관찰하였다

Keywords: 환원그래핀(Reduced graphene oxide), 종이(Paper), 주름(Wrinkle), 전단 탄성 계수(Shear modulus), 신축성(Stretchability)