  • Evaluation of Mechanical and Vibration Characteristics of Laminated Damping Aluminum Panel for Automobile Components
  • Sung-Youl Bae, Ki-Man Bae, Yun-Hae Kim
  • Composites Convergence Team, Korea Textile Machinery Convergence Research Institute, Gyeongsan 38542, Korea, R&D Center, Iljitech, Gyeongsan 38471, Korea, Department of Ocean Advanced Materials Convergence Engineering, Korea Maritime and Ocean University, Busan 49112, Korea
  • 자동차 부품용 알루미늄 접합 제진 패널의 기계적 특성 및 진동 특성 평가
  • 배성열, 배기만, 김윤해
Abstract
The objective of this research is to study the mechanical and vibration characteristics of vibration damping aluminum panels for automotive parts. For this purpose, the test and simulation results of aluminum-resin hybrid materials and aluminum sheet materials were compared. Tensile strength and elastic modulus of the hybrid material were approximately 10% lower than aluminum sheet. Also, it was showed that the hybrid material have lower natural frequency than aluminum sheet, and it was confirmed that loss factor increases as the thickness of resin increases. Finally, it is confirmed that the test results and the analysis results are similar with each other and the performance prediction of the materials are possible by FEA.

본 연구의 목적은 자동차용 부품에 적용하기 위한 알루미늄 접합 제진 패널에 대한 기계적 특성 및 진동 특성을 도출하기 위한 것이며, 이를 위해서 알루미늄 하이브리드 소재와 알루미늄 원소재의 시험 및 시뮬레이션 결과가 상호 비교되었다. 알루미늄 제진 패널 및 알루미늄 원소재의 인장강도 평가를 통해서 알루미늄 하이브리드 소재의 인장강도 및 인장탄성계수가 알루미늄 원소재 대비 약 10% 내외로 낮음을 확인할 수 있었다. 소재 단위의 해석 및 시험을 통해서 하이브리드 소재가 원소재 대비 낮은 고유진동수를 나타냄을 확인하였고, 하이브리드 소재를 구성하는 수지의 두께가 높아질수록 손실계수가 상승됨을 확인하였다. 또한, 기계적 특성 평가 모사 시뮬레이션을 통해 시험결과와 시뮬레이션 결과가 잘 일치하며, 유한요소해석을 통한 소재의 성능예측이 가능함을 확인할 수 있었다.

Keywords: Vibration damping aluminum panel, Vibration characteristics, Finite element analysis, Viscoelastic damping polymer

Keywords: 알루미늄 제진 패널, 진동 특성, 유한요소해석, 점탄성고분자