ABSTRACT: This paper presents the slip behavior of composite fabrics by high speed resin flow in high pressure resin transfer molding. In order to observe the fiber deformation behavior, we constructed the measuring equipment for friction coefficient between fiber and mold, and the monitoring system for deformation of fiber preform in highpressure RTM process. Coulomb friction coefficient and hydrodynamic friction coefficient between fiber preform and mold were measured and the external force induced by fluid flow causing the deformation of fiber preform was measured. Friction force calculated by friction coefficient and the external force upon fiber deformation were compared, which showed that preform deformation occurred when the external force was bigger than the friction force. The slip behavior of the fiber preform was mainly influenced by the volume fraction of fiber preform and the friction coefficient.

초 록: 본 연구에서는 고압 RTM 공정에서 고속 수지 유동에 의한 섬유 보강재의 변형 거동에 관한 연구를 진행 하였다. 이를 위해 섬유와 금형의 마찰계수 측정 장치와 고압 RTM 공정을 모사하여 preform 변형을 평가하는 장 치를 구축하였다. 마찰계수 측정 장치를 통해 금형-섬유 간 Coulomb 마찰계수와 수력학적 마찰 계수를 측정하였 고, preform 변형 평가 장치를 통해 preform의 변형이 발생할 때의 유체에 의해 작용하는 외력의 힘을 측정하였다. 마찰계수를 이용하여 마찰력을 구하고 외력과 비교하여 직물의 슬립(slip) 여부를 판별할 수 있었다. 유체에 의해 섬유에 작용하는 외력이 섬유와 금형 사이의 마찰력보다 커지게 되면 직물이 움직이는 것으로 관찰 되었으며, 이 는 섬유의 체적률과 마찰계수에 주로 영향을 받는 것으로 나타났다.

Keywords: High-pressure resin transfer molding, composite, fiber deformation, friction

Keywords: HP-RTM , 복합재료, 섬유 변형, 마찰 력