Original Article
  • Investigation of Adhesion property between Glass Fiber Reinforced Plastic and Polyurethane adhesives on Peel strength under Cryogenic temperature
  • Min-Young Shon*+, Jae-Kwang Lee, Jeong-Lak Hong
  • 극저온에서 유리섬유강화플라스틱 표면의 유리섬유와 폴리우레탄 접착제간의 접착특성이 전체 박리강도에 미치는 영향에 대한 연구
  • 손민영(삼성중공업), 이재광(삼성중공업), 홍정락(삼성중공업)
Abstract
Adhesive joints are widely used for structural joining applications in various fields and environmental conditions. Polyurethane adhesive is using for LNG carrier with cryogenic temperature condition. Even if similar polyurethane adhesive is used for different substrate, it shows different adhesion properties. Specially, variation of adhesion properties depending on the resin system or fiber is very important factor for selection of adhesive on industrial application. In present study, we got different peel strength according to the different test temperature when different polyurethane adhesive was used for same fiber reinforced composite. The main cause was investigated using by SEM and it was proven that the different adhesion property between glass fiber on composite surface and polyurethane adhesives at cryogenic temperature.

접착제에 의한 접합기술은 다양한 목적과 환경에서 널리 사용되는 방법이다. 그 중 우레탄 접착제는 저온에서의 우수한 접착 특성으로 인하여 액화천연가스 운반선과 같은 극저온 환경의 접착에 사용되고 있다. 유사한 우레탄 접착제라도 각기 다른 기재와의 접착특성을 갖게 된다. 특히 기재에 사용된 수지의 종류와 섬유와의 상응성에 따른 접착력의 변화는 산업현장에서의 접착제 선정에 매우 중요한 인자로 작용된다. 본 연구에서는 서로 다른 제조사의 우레탄 접착제를 사용하여 동일한 유리섬유강화복합재료에 접착하였을 때 실험 온도에 따른 다른 경향의 박리강도를 얻었다. 그 원인을 주사전자현미경을 사용하여 검토하였으며, 실험 결과 극저온에서 접착제와 복합재료 수지간의 접착력은 거의 유사하였으나 접착제와 기재에 노출된 유리섬유간의 접착력이 달라짐에 따른 원인으로 확인하였다.

Keywords: Peel strength, Glass fiber, Polyurethane, GFRP

Keywords: 박리강도, 유리섬유, 폴리우레탄, 유리섬유강화플라스틱