  • A Study on the energy absorption characteristics of GFRP circular tubes fabricated by the filament winding method
  • Geo-Young Kim*, Jeong-Seo Koo**+
  • 필라멘트 와인딩 공법 GFRP 원형 튜브의 에너지 흡수특성에 관한 연구
  • 김거영(서울산업대학교 철도전문대학원), 구정서(서울산업대학교 철도전문대학원)
Abstract
In this paper, quasi-static crushing tests of composite circular tubes under axial compression load are conducted to investigate the energy absorption characteristics. Circular tubes used for this experiment are glass/epoxy (GFRP) composite tubes which are fabricated by the filament winding method. One edge of the composite tube is chamfered to reduce the initial peak load and to prevent catastrophic failure during crushing process. Energy absorption characteristics vary significantly according to the constituent materials, fabrication conditions, tube geometry and test condition. In tube geometry, according as inner diameter increase, unstable crush mode is caused by local buckling of delamination, but control of the fiber orientation should help composite tubes get stable crush mode.

본 논문에서는 복합재 원형튜브의 에너지 흡수 특성을 평가하기 위해 준정적 압괴실험을 시행하였다. 사용된 시편은 필라 멘트 와인딩 공법으로 제작된 GFRP(유리섬유/에폭시수지) 원형 튜브이다. 복합재 튜브의 에너지 흡수 특성 분석을 위한 파라미터로서 튜브의 트리거메커니즘, t/D, 섬유배향각 등을 고려하여 그 특성을 비교하였다. 튜브의 형상 측면에서 튜브 직경이 커짐에 따라 delamination에 의한 국부좌굴 발생빈도가 증가하게 되어 불안정한 압괴모드가 발생하는데 이러한 현상은 섬유 배향각을 조정하여 안정적인 압괴모드를 도출할 수 있었다.

Keywords: quasi-static crushing test, axial compression load, trigger mechanism, energy absorption characteristics,filament winding, mean crush force

Keywords: 준정적 압괴시험, 축압력 하중, 트리거 메커니즘,에너지 흡수 특성, 필라멘트 와인딩 공법, 평균 압괴 하중