Expanded graphite/carbon fiber hybrid conductive polymer composites were fabricated by the preform molding technique. The conductive fillers were mechanically mixed with a phenol resin to provide an electrical property to composites. The conductive filler loading was fixed at 60wt.% to accomplish a high electrical conductivity. Expanded graphites were excellent in forming a conductive networking by direct contacts between them while it was hard to get the high flexural strength over 40MPa with using only expanded graphite and phenol resin. In this study, carbon fibers were added in composites to compensate the weakened flexural strength. The effect of carbon fibers on the mechanical and electrical properties was examined according to the weight ratio of carbon fiber. As the carbon fiber ratio increased, the flexural strength increased until the carbon fiber ratio of 24wt.%, and then decreased afterward. The electrical conductivity gradually decreased as the increase of the carbon fiber ratio. This was attributed to the non-conducting regions generated among the carbon fibers and the reduction of the direct contact areas between expanded graphites.

본 연구에서는 팽창흑연/탄소섬유 혼합 보강 전도성 고분자 복합재료를 2단계 성형 공법으로 제조하였으며, 탄소섬유의 첨가가 전도성 고분자 복합재료의 전기적, 기계적 특성에 미치는 영향을 고찰하였다. 전도성 충진재들은 고분자 수지와 기계적으로 혼합되었으며 이를 통하여 복합재료가 전기적 특성을 가지도록 하였다. 팽창흑연은 입자 간 접촉 면적이 넓기 때문에 복합재료 내 전도성 네트워킹의 형성에 매우 유리하지만, 팽창흑연과 고분자 수지만을 사용하여 상기 공정으로 복합재료를 제조할 경우 우수한 기계적 강도를 얻기가 어렵다. 따라서 이를 보완하기 위하여 탄소섬유를 복합재료에 첨가 하였으며 전기적 기계적 물성을 바탕으로 탄소섬유의 혼합 비율을 최적화 하였다. 굽힘 강도는 탄소섬유의 충진 비율이 증가할수록 섬유에 의한 강화 효과에 의하여 증가 하지만, 32wt.% 이상에서는 오히려 감소하였다. 이는 여분의 탄소섬유들이 공극을 발생시켜 응력집중이 발생하기 때문으로 판단된다. 전기 전도도는 탄소섬유의 비율이 증가할수록 전도성 공백이 발생하고 팽창흑연의 전도성 네트워킹이 저해되기 때문에 계속 감소한다.

Keywords: Expanded Graphite, Conductive Polymer Composites, Electrical Conductivity, Flexural Strength

Keywords: 팽창흑연, 전도성 고분자 복합재료, 전기 전도도, 굽힘 강도