  • Evaluation on Thermal Shock Damage of Smart Composite using Nondestructive Technique
  • Jin-Kyung Lee*, Young-Chul Park**, Kyu-Chang Lee***, Joon-Hyun Lee****
  • 비파괴 기법을 이용한 스마트 복합재료의 열충격손상평가
  • 이진경(동의대학교), 박영철(동아대학교), 이규창(포항과학기술연구원), 이준현(부산대학교)
Abstract
Tensile residual stress is occurred by difference of coefficients of thermal expansion between fiber and matrix is one of the serious problems in metal matrix composite(MMC). TiNi alloy fiber was used to solve the problem of the tensile residual stress as the reinforced material. TiNi alloy fiber improves the tensile strength of composite with occurring of compressive residual stress in the matrix by its shape memory effect. A hot press method was used to create the optimal fabrication condition for a Shape Memory Alloy(SMA) composite. The bonding effect of the matrix and the reinforcement within the SMA composite by the hot press method was strengthened by cold rolling. In addition, acoustic emission technique was used to quantify the microscopic damage behavior of cold rolled TiNi/Al6061 shape memory alloy composite at low temperature. The damage degree for the specimen that underwent thermal shock cycles was also discussed.

금속복합재료에서는 강화재와 기지재 사이의 열팽창계수 차이에 의해 복합재료 내부에 잔류응력이 남아있어 복합재료 전체의 강도저하를 가져온다. 본 연구에서는 TiNi 형상기억합금을 강화재료로써 이러한 잔류응력 문제를 해결하기 위하여 이용하였다. TiNi 형상기억합금은 형상기억효과를 이용하여 복합재료의 잔류응력문제를 해결할 뿐만 아니라 복합재료의 인장강도를 증가시키는 역할을 한다. 핫프레스 방법에 의해 제작된 형상기억복합재료의 강도증가를 위하여 냉간압연을 실시하여 실험을 실시하였다. 이와 같이 제작된 형상기억복합재료의 저온에서의 미시적 손상거동을 평가하기 위하여 음향방출기법을 이용하였다. 또한 열충격을 받은 시험편의 손상에 대한 연구도 이루어졌다

Keywords: Metal Matrix Composite, Residual Stress, Shape Memory Alloy, Cold Rolling, Acoustic Emission

Keywords: 금속복합재료, 잔류응력, 형상기억합금, 냉간압연, 음향방출