In this paper, the sandwich panel composites consisting of core material and face sheet were studied to evaluate the mechanical properties, noise level and fire resistance including flammability, smoke, and toxicity. Four types of sandwich panel were prepared using various kinds of panel and honeycomb materials. It was observed that Al honeycomb/AI skin composite materials had the excellent flatwise tensile strength and edgewise compressive strength compared with other types of composites. The flatwise compressive strength and flexural strength of Nomex honeycomb/AI skin composite were higher than those of other composites. PMI form/AI skin composite showed the higher core shear strength and facing bending strength. From the experimental results of flame resistance tests, it can be said that the phenol based skin composite has the excellent flame retardation properties, which are similar to those of the commercial skin composites. ~

본 연구에서는 샌드위치 패널 구성 요소인 면재와 심재를 변화시켜 4종류의 샌드위치 패널을 제작하였다. 그리고 제작된 샌드위치 패널의 기계적 특성과 철도차량 개발시 중요한 요인으로 작용하는 음향투과 특성 그리고 화재에서의 안정성을 확인하기 위하여 난연특성 실험을 통하여 샌드위치 패널의 특성을 검토하고자 하였다. 샌드위치 패널의 기계적 특성은 알루미늄 면재 + 알루미늄 하니컴 심재로 구성된 샌드위치 패널이 면방향 인장강도와 변방향 압축강도 특성에서 우수하며 알루미늄 면재 + 노멕스 하니컴 심재로 구성된 샌드위치 패널은 면방향 압축강도와 굽힘강도가 우수한 것으로 확인되었다. 알루미늄 면재 + PMI 포옴 심재로 구성된 샌드위치 패널은 심재의 전단강도 및 면재의 굽힘강도가 우수하였다. 난연성 시험에서는 phenol 수지 면재와 2종의 외국 면재는 모든 시험 결과에서 유사한 결과를 확인하였다.