  • A Study on Lightweight Design of Double Deck High-Speed Train Hybrid Carbody Using Material Substitution and Size Optimization Method
  • Jae-Moon Im, Min-Ho Jung, Jong-Yeon Kim, Kwang-Bok Shin
  • Rolling Stock R&D Center, Dawonsys Co., Ltd., Department of Mechanical Engineering, Hanbat National University
  • 소재대체법과 치수최적화 기법을 이용한 2층 고속열차 하이브리드 차체 구조물의 경량 설계 연구
  • 임재문, 정민호, 김종연, 신광복
Abstract
The purpose of this paper is to suggest a lightweight design for the aluminum extrusion carbody structure of a double deck high-speed train using material substitution and size optimization method. In order to conduct material substitution, the topology optimization was used to determine the application parts of sandwich composites at the carbody structures. The results of analysis showed that sandwich composites could be applied at roof and 2nd underframe. The size optimization was used to determine thickness of the aluminum extruded and carbon/epoxy composite. The design variable, state constraint and objective function were formulated to solve the size optimization, and then, the feasible design was presented by these conditions. The results of the lightweight design showed that the weight of double deck high-speed train hybrid carbody could be reduced by 2.18(17.70%) tons.

본 논문의 목적은 소재대체법과 치수최적화 기법을 이용한 2층 고속열차 알루미늄 압출재 차체의 경량 설계를 제시하는 것이다. 소재대체법을 수행하기 위해 위상최적화 기법을 이용하여 차체 구조물의 샌드위치 복합 재 적용 부위를 결정하였다. 해석결과, 루프와 2층 언더프레임에 샌드위치 복합재가 적용 가능함을 보여주었다. 치수최적화는 알루미늄 압출재와 카본/에폭시 복합재의 두께를 결정하는데 사용되었다. 치수최적화를 수행하기 위해, 설계변수, 제약조건, 목적함수를 정식화 하였으며 이러한 조건에 의해 유효설계를 도출하였다. 경량 설계의 결과로 2층 고속열차 하이브리드 차체의 무게를 2.18 ton(17.70%)까지 줄일 수 있음을 보여주었다.

Keywords: Lightweight design, Size optimization, Material substitution, Topology optimization, Sandwich composites