  • Fabrication of Ceramic Particulate Reinforced Steel Composites by Liquid Pressing Infiltration Process
  • Seungchan Cho, Yeong-Hwan Lee, Seongmin Ko, Hyeon Jae Park, Donghyun Lee, Sangmin Shin, Ilguk Jo, Sang-Kwan Lee, Sang-Bok Lee
  • Composites Research Division, Korea Institute of Materials Science, Changwon, Korea
  • 용융가압함침공정을 이용한 세라믹 입자 강화 철강복합재료의 제조성 검증
  • 조승찬, 이영환, 고성민, 박현재, 이동현, 신상민, 조일국, 이상관, 이상복
Abstract
Various ceramic particulate such as TiC, TiB2, Al2O3 reinforced SUS431 matrix composites were successfully fabricated by a novel liquid pressing infiltration process. Microstructures of the SUS431 composite were analyzed to determine manufacturability of composites. Al2O3–SUS431 composite had lots of defects due to poor wettability between the Al2O3 and steel matrix. On the other hand, TiC was uniformly dispersed in the SUS431 matrix than TiB2 and Al2O3 due to good wettability and interfacial properties.

본 연구에서는 용융가압함침 공정을 이용하여 TiC, TiB2, Al2O3 세라믹 입자가 분산된 SUS431 금속복합재료를 제조하고 미세조직을 분석하여 세라믹 입자에 따른 제조성에 대해 검토하였다. 젖음성이 나쁜 Al2O3의 경우 내부에 결함이 다수 존재함을 알 수 있었으며, TiB2 및 TiC 입자 강화 복합재의 경우 상대적으로 결함이 적고 강화재가 균일 분산되었음을 확인하였다. 특히, TiC–SUS431 복합재료의 경우 TiC와 Fe계 기지합금의 우수한 젖음성 및 용융가압함침공정 적용으로 우수한 계면 특성을 가지며 결함이 적고 균일한 미세조직을 가지는 것을 확인하였다.

Keywords: Metal matrix composite, Titanium carbide, Titanium boride, Aluminum oxide, Liquid pressing infiltration

Keywords: 금속복합재료, 탄화 티타늄, 붕화 티타늄, 산화 알루미늄, 용융가압함침

This Article

  • 2018; 31(4): 117-121

    Published on Aug 31, 2018