The RFI process can be applied to very thick structures without limiting the resin viscosity. When the proper thickness of the resin film cannot be set, the resin film creates either the non-impregnated section or the excessive resin contents and this leads to the deterioration of mechanical properties. Therefore, this study proposed a method for setting the resin film thickness in the RFI process. The fiber compaction behavior test was proposed by setting the proper resin film thickness and the properties of composites were evaluated through short beam shear strength test, compression test and porosity measurement to verify the proposed method. The evaluation of physical properties of composites was conducted and an appropriate level of resin film thickness was found based on the results of fiber compaction behavior test.

RFI 공정은 수지 점도에 제한이 없어 매우 두꺼운 구조물에도 적용이 가능하다. 수지필름 두께를 설정할 때 수지필름의 두께가 얇은 경우 미함침 구간이 발생하여 기계적 물성이 저하되고, 수지필름 두께가 두꺼운 경우 필요이상의 여분 수지가 발생하게 된다. 따라서 본 연구에서는 RFI 공정에서 수지필름 두께 설정을 위한 방법을 제시하였다. 적정 수지필름 두께를 설정하는 방법으로 섬유압착거동 시험을 제시하였고, 제시된 방법의 검증을 위해 숏빔전단강도시험, 압축시험, 기공률 측정을 통해 복합재 물성을 평가하였다. 복합재 물성 평가 결과, 섬유 압착거동시험 결과를 바탕으로 적정 수준의 수지필름 두께를 찾을 수 있었다.

Keywords: Resin Film Infusion process, Out of Autoclave, Resin film thickness, Fiber compaction behavior

Keywords: RFI 공정, OoA, 수지필름 두께, 섬유압착거동