Original Article
  • Study on the Prediction of Dimension Variation due to the Temperature Rises of the Composite Material and Box Beam Type Mold Steel
  • Ho-Sang Kim*†, Chan-Hee Lee*, Won-Gi Lee*
  • *Institute for Advanced Engineering
  • 복합재료를 이용한 박스빔 형태 금형의 온도상승에 따른 치수 변화 예측에 관한 연구
  • 김호상*† · 이찬희* · 이원기*
Abstract
Composite material and mold steel can be expanded differently with the temperature gradients during the forming process because their coefficients of thermal expansions are not the same. Therefore, in order to manufacture the product with accuracy, it is necessary to verify that the forming pressure on the surface of the composite material is maintained to the required level from the material supplier. In this paper, the pressure between the composite material and mold due to the temperature difference was predicted by finite element analysis and the accuracy of predicted value was verified by measuring the thermal expansions of mold steel by the ruler. The predicted value by finite element analysis is closely in agreement with one by the experiment within the required tolerance value of ±0.05 mm.

복합소재와 금형강 간에는 열팽창계수의 차이로 인하여 성형 과정 중의 온도 구배에 따라 다른 열팽창길 이를 갖는다. 따라서 금형 내에 복합소재를 삽입하여 성형을 하는 경우 복합소재의 표면에 작용하는 압력이 소재 의 업체에서 추천하는 성형 압력을 유지하는지를 확인할 필요성이 있다. 본 연구에서는 온도의 차이에 따른 복합 소재와 금형 사이의 압력을 유한요소해석법을 사용하여 예측하였으며 열팽창에 따른 금형의 길이를 측정함으로 써 해석의 정확성을 검증하였다. 각 온도에서의 해석과 실험값의 차이로써 매우 근사한 값을 얻을 수 있었으며, 틈새 예측 값의 목표치인 ±0.05 mm 안에 들어오는 것을 확인하였다. 이를 통하여 복합소재에 작용하는 압력을 추 정한 해석값이 신뢰할 수준임을 알 수 있었다.

Keywords: Composite material, Box beam, Mold, Temperature rise, Finite element analysis, Pressure

Keywords: 복합재료, 박스빔, 금형, 온도상승, 유한요소해석, 압력

This Article

  • 2018; 31(1): 12-16

    Published on Feb 28, 2018