The shrinkage distribution of a dental composite (Clearfil AP-X, Kuraray, Japan) used for dental restoration was observed using a digital image correlation method. In order to analyze the shrinkage distribution formed during and after light irradiation, digital images were taken with different photographing conditions for each period. Optimal photographing conditions during LED irradiation were obtained through a preliminary experiment in which the exposure time was applied from 0.15 ms to 0.55 ms in 0.05 ms intervals. The DIC analysis results showed that the strain was non-uniform. For the initial 20 s of light irradiation the composite resin shrank to the level of 50~60% of the final curing shrinkage. Such large shrinkage amount of the composite resin lump affected the tensile stress concentration near the adhesive region between the composite resin and the substrate.

손상된 치아의 복구에 사용되는 재료인 치과용 복합레진 Clearfil AP-X (Kuraray, Japan)을 대상으로 디지털 이미지 상관법을 이용하여 광중합 시 발생하는 수축분포를 관찰하였다. 디지털 이미지 상관분석법을 위해, CCD 카메라를 이용하여 광조사 중과 광조사 이후의 촬영 조건을 달리하여 사진을 획득하였다. 광조사중의 최적의 촬 영 조건을 설정하기 위하여 노출시간을 0.15 ms부터 0.55 ms까지 0.05 ms 간격으로 촬영한 사전 실험을 통해 촬영 조건을 획득하였다. DIC 분석 결과 복합레진의 비균일한 수축 분포를 관찰하였으며 복합레진의 중심 부분에서 시 편의 계면부보다 좀 더 자유로운 유동성으로 더 큰 수축이 발생하였다. 복합레진의 중합수축은 초기 20 s 의 광조 사에서 최종경화수축률의 50~60% 수준까지 발생하였다. 이러한 치과용 복합레진의 큰 수축량은 레진/기질계면 근처에서 인장응력이 집중하도록 영향을 주었다.

Keywords: Dental composite resin, Digital image correlation, Polymerization shrinkage, Shrinkage distribution, Methacrylate-based composite resin, Dental restoration

Keywords: 치과용합레진, 디지털이미지상관, 중합수축, 수축분포, Methacrylate 기질 복합레진, 치아수복