  • The Analysis on Properties of Epoxy/MWCNT for Bonding CFRP to Steel Plates
  • Sung-Hun Yoo†, Il-Jun Kwon, Dong-Woo Shin, Sung-Min Park, Jeong-Hyun Yeum
  • DYETEC Institute, Daegu, Korea†DYETEC Institute, Daegu, Korea;Kyungpook National University, Daegu, Korea
  • CFRP와 금속 재료의 접합을 위한 epoxy/MWCNT의 특성 분석
  • 유성훈† · 권일준 · 신동우 · 박성민 · 염정현
Abstract
The effect of a multi walled carbon nanotubes (MWNCT) on the adhesive properties and thermal properties of epoxy were studied by double lap-shear tests. Epoxy/MWCNT resins were prepared from a different amount of the MWCNT incorporated into the epoxy resins (araldite 2011). Steel plates and carbon fiber reinforced plastics (CFRP) were chosen as materials. Mechanical tests were performed by a universal testing machine (UTM). The analysis of thermal properties were conducted by a thermogravimetric analyzer (TGA) and a differential scanning calorimetry (DSC). The fracture surface morphology was examined using a scanning electron microscopy (SEM) and optical microscope. Compared to neat epoxy, it was found that the mechanical properties of epoxy/MWCNT resins are increased.

에폭시 수지의 열적 특성과 접합 특성에 대해 다중벽 탄소 나노 튜브 (MWCNT)의 효과가 이중 중첩 전단시험에 의해 연구되었다. Epoxy/MWCNT 복합 수지는 에폭시 수지(araldite 2011)에 다양한 질량 분율로 MWCNT를 분산하여 제조되었다. MWCNT의 효과를 확인하기 위해 접합강도 시험이 열특성 변형 만능재료시험기에 의해 진행되었고 충격강도 시험이 ASTM D256에 따라 진행되었다. 금속 판재와 탄소섬유강화복합재료가 실험 재료로써 사용되었으며, 열적 안정성 분석은 열 중량 분석기와 시차 주사 열량기에 의해 진행되었다. 또한 접합강도 시험 후 시편의 형태학적 특성은 주사전자현미경에 의해 관찰되었고 파괴거동을 알아보기 위하여 광학현미경을 사용하였다. 에폭시 수지와 비교하였을 때 epoxy/MWCNT 복합 수지가 물리적 특성이 향상되는 것을 나타내었다.

Keywords: Multi walled carbon nanotubes,Carbon fiber reinforced plastics,Epoxy resin,Steel material,Adhesive strength

Keywords: 다중벽 탄소 나노 튜브,탄소섬유강화복합재료,에폭시 수지,금속 재료,접합강도

This Article

  • 2017; 30(3): 215-222

    Published on Jun 30, 2017