In this study, integrated co-bonded panels with the same configuration of hat stiffeners were fabricated and measured for ply waviness phenomenon. Total specimens consisted of 2 types; 1) the general co-bonded panel and 2) the co-bonded panel with caul plate made of carbon epoxy composite materials. The first general co-bonded panel specimen exhibited that laminate thickness on the stiffener location area was much thicker than the non stiffener area and, there was ply waviness with 0.61 mm height and 3.29 mm length. In the second co-bonded panel specimen, the reduced waviness with 0.22 mm height and 1.37 length resulted in more than 50% improvements, which is due to the uniform pressure distribution of co-bonded interface by caul plate.

본 연구에서는 동일한 구조의 모자형 보강재를 이용하여 일체형 동시접착 구조의 보강패널시편을 제작하였다. 일반적인 동시접착 보강패널 시편과 탄소에폭시 복합재를 이용하여 제작된 카울플레이트(Caul Plate)를 적용한 동시접착 보강패널 시편의 2가지 형태 시편을 제작하였으며 일반 동시접착 보강패널 시편에서는 패널 상에서 보강재가 적용되지 않은 부위가 적용된 부위보다 더 두꺼운 패널 두께를 가지고 그 연결부위에는 0.61 mm 높이 및 3.29 mm 길이의 플라이웨이브 현상이 나타났다. 카울플레이트가 적용된 보강패널 시편에서는 보다 균일한 압력 전달로 인하여 0.22 mm 높이와 1.37 mm 길이의 완화된 웨이브 현상을 보이면서 약 50% 이상 개선된 결과를 얻을 수 있었다.

Keywords: Composites, Integrated structure, Co-bonded structure, Ply waviness

Keywords: 복합재, 일체형구조, 동시접착구조, 플라이 웨이 브