  • Enhancement of the Mechanical Properties of CNT Fibers Synthesized by Direct Spinning Method with Various Post-Treatments
  • Jin-seok Kim*,**, Junbeom Park*, Seung Min Kim*, L.K Kwac**†, Jun Yeon Hwang*†
  • *Korea Institute of Science and Technology, Jeonbuk, * Korea Institute of Science and Technology, Jeonbuk, Corresponding author (E-mail: Junyeon.Hwang@kist.re.kr), **Department of Carbon Convergence Engineering, Jeonju University, Jeonbuk, ** Department of Carbon Convergence Engineering, Jeonju University, Jeonbuk, Corresponding author (E-mail: kwac29@jj.ac.kr)
  • 직접 방사법으로 합성된 탄소나노튜브 섬유의 기계적 특성 향상
  • 김진석*,** · 박준범* · 김승민* · 곽이구**† · 황준연*†
Abstract
Recent studies regarding the properties of carbon nanotubes (CNT) have made remarkable progress in CNT fibers research. However no CNT fibers showed the properties of CNTs because CNTs in fibers have weak interfacial bonding with low shear modulus in the pristine form. Thus, it is upmost interest to develop and employ post-production treatments to the CNT fibers that would potentially improve their properties. In this study, post- treatments resulted in improvement of strength of CNT fibers up to 40%.

최근탄소나노튜브(CNT)고유의특성을충분히발현하면서,섬유화를통해장점을극대화할수있는탄 소나노튜브 섬유 합성 방법 및 후처리 공정들이 많은 관심을 받아왔다. 그러나 개별 탄소나노튜브가 다발형태로 집속되어지는 과정 중, 탄소나노튜브 상호간 약한 계면결합력과 전단특성으로 인하여 원하는 섬유 물성을 확보하 기 어려운 문제점을 갖고 있다. 이를 해결하기 위해서 본 연구에서는 Direct Spinning 방법을 통한 탄소나노튜브 의 연속적인 합성과 다양한 후처리 방법을 이용하여 탄소나노튜브 섬유의 기계적 특성을 조사하였다. 플라즈마 후처리를 통하여 측정된 탄소나노튜브 섬유의 기계적 물성은 본래의 섬유보다 최대 40%가 증가됨을 확인하였다.

Keywords: Direct spinning, Chemical Vapor Deposition, Carbon Nanotube Fiber, Plasma Treatment

Keywords: 직접방사, 화학기상증착법, 탄소나노튜브 섬유, 플라즈마 처리