ABSTRACT: Carbon fiber (CF) reinforced polypropylene (PP) compositeis was increased to amount consumed. In this study, recycle of composites by recycle times. CF was containing 20%. Mechanical and interfacial propertis of CF/PP was evaluation for number of recycle time. Mechanical assessment of CF/PP was tension, bending, fatigue tension test and izod test method. Interfacial assessment of CF/PP was wettability test and FE-SEM of fracture surface method. Fiber and matrix was changed to recycle time. The more recycle of CF/PP, the more interfacial bonding was decreased. Because fiber and matrix was damaged to thermal damage. And then reinforced CF was shorter than original shape.

초 록: 탄소섬유(CF) 강화 폴리프로필렌(PP) 복합재료의 수요는 증가되고 있다. 본 연구에서는 재활용 횟수에 따 라 변화되는 복합재료의 물성 변화를 관찰하였다. CF 함량을 20% 함량으로 조성한 복합재료에 대해서 재활용 횟 수에 따른 기계적 물성 평가를 진행하였다. 인장, 굴곡, Izod 동적 피로 실험에 따른 영향을 확인하였다. CF/PP 복 합재료의 계면 물성을 평가하기 위해 젖음성 평가와 파단면을 FE-SEM으로 확인하였다. 재활용 횟수에 따라 섬유 와 기지는 변화된다. CF/PP 복합재료는 재활용 할수록 섬유와 기지간의 계면에 열 데미지와 분쇄 과정에 의한 결 합력 감소가 확인하였다.

Keywords: recycle, composite materials, polypropylene, crystallinity

Keywords: 재활용, 복합재료, 폴리프로필렌, 결정성