  • Experimental Testing of Curved Aluminum Honeycomb/CFRP Sandwich Panels
  • Rene Roy*, Yong-Bin Park*, Jin-Hwe Kweon*†, Jin-ho Choi**
  • 곡면형상의 알루미늄 하니콤/CFRP 샌드위치 패널에 관한 실험적 연구
  • 롸르네* · 박용빈* · 권진회*† · 최진호**
Abstract
This paper presents the fabrication and 3-point flexion testing of carbon fiber reinforced polymer (CFRP) composite face/aluminum honeycomb core sandwich panels. Specimen sandwich panels were fabricated with three honeycomb types (3.18 mm, 4.76 mm, and 6.35 mm cell size) and three panel radii (flat, r = 1.6 m, r = 1.3 m). The curved sandwiches were fabricated normally with the core in the W-direction. The tensile mechanical properties of the CFRP 2 × 2 twill fabric face laminate were evaluated (modulus, strength, Poisson's ratio). The measured values are comparable to other CFRP fabric laminates. The flat sandwich 3-point flexion test core shear strength results were 11- 30% lower than the manufacturer published data; the test set-up used may be the cause. With a limited sample size, the 1.3 meter panel curvature appeared to cause a 0.8-3.8% reduction in ultimate core shear strength compared to a flat panel.

본 논문에서는 탄소섬유강화플라스틱 면재와 알루미늄 샌드위치 심재를 가지는 복합재 샌드위치의 제조와 3절점 굽힘 실험에 대해 연구하였다. 시편은 3가지 하니컴 종류(3.18 mm, 4.76 mm, 6.35 mm의 셀 크기)와 3가지 곡 률 반지름(평판, r = 1.6 m, r = 1.3 m)을 가지도록 제작하였다. 샌드위치 곡률의 기준은 W-방향을 기준으로 제작 하 였다. CFRP 2 × 2 트윌의 인장에서 기계적 물성치(탄성계수, 강도, 푸아송 비)를 측정하여 그 값들을 다른 CFRP 섬 유 적층판의 값과 비교하였다. 실험결과 평판 샌드위치 패널의 3절점 굽힘 실험에서 심재의 전단강도는 공개된 데 이터에 비해 11-30% 낮게 나왔다. 제한된 시편 크기에서 1.3미터 곡률을 가지는 패널은 평판 패널에 비해 심재의 극 한 전단강도가 0.8-3.8% 감소한 것으로 나타났다.

Keywords: sandwich, honeycomb, carbon fiber reinforced polymer, curvature, flexion

Keywords: 샌드위치, 하니컴, 탄소섬유강화플라스틱, 곡률, 굽힘