In this paper, the variation of mechanical properties of T800 carbon/epoxy composites according to the forming pressure, which was referred to previous studies on a filament winding process, were investigated. The specimens of all the tests were fabricated by an autoclave de-gassing molding process controlling forming pressure (absolute pressures of 0.1MPa, 0.3MPa, 0.7MPa including vacuum) and water jet cutting after fabricating composite laminates. Various tensile tests were performed for in-plane properties and interlaminar properties were also measured by using Iosipescu test jig. Fiber volume fraction was measured to correlate the property variation and the forming pressure. This properties are expected to be utilized in the design of Type III pressure vessel for hydrogen vehicles which uses the same carbon fiber (T800 carbon fiber) for the filament winding process.

본 논문에서는 필라멘트 와인딩 시 장력에 의해 압밀을 유발하는 압력을 선행연구자들의 연구를 참조하여 결정한 후 T800 탄소섬유/에폭시 복합재료의 기본적인 물성과 성형압력 변화에 따른 면 내·외의 물성 변화를 측정하였다. 실험 시편은 오토클레이브 진공백 성형을 통해 압력(절대압력 0.1MPa, 0.3MPa, 0.7MPa)을 조절하여 제조되었다. 모든 시편은 적층판 형태로 경화된 후 워터젯을 이용하여 시편 모양으로 절단되었으며, 층간 전단시편의 V-노치는 밀링가공을 통하여 제작되었다. 평면 내 물성을 위해 다양한 인장실험이 실시되었으며, 평면 외 물성을 측정하기 위해 층간 전단 실험이 수행되었다. 성형압력과 물성 변화를 관련시키기 위해 시편의 섬유 부피분율을 측정하였다. 본 연구에서 측정된 물성은 동일한 탄소섬유 (T800 탄소섬유)를 사용하여 필라멘트 와인딩 공정으로 제작되는 차량용 Type III 수소저장용기의 설계에 유용하게 활용될 수 있을 것으로 기대된다.

Keywords: T800 carbon/epoxy composite, Forming pressure, Filament winding, Interlaminar shear test

Keywords: T800 탄소섬유/에폭시 복합재료, 성형 압력, 필라멘트 와인딩, 층간전단 실험