The failure strengths and modes in carbon fiber reinforced polymeric composites, with two serial bolt-fastened composite joints, were investigated to evaluate the typical joint configurations of composite components. The parametric studies were performed experimentally at room temperature dry and elevated temperature wet, 82.2℃ on several different laminate configurations. Based on the experimental data presented, two basic load-displacements curves are observed. Each failure mode has the characteristic curve. It is showed that the bearing failure mode occurs in elevated temperature wet condition. It is analysed that the strength of bearing failure mode is not highly depending on the effective modulus of specimen. The failure strength at elevated temperature wet is decreased by the cause of interfacial deterioration between fiber and matrix with moisture absorption.

복합재 부품의 전형적인 조인트 형태를 평가하기 위해서, 2열 볼트 체결 탄소섬유강화 복합재의 파손강도와 파손 모드에 대하여 연구를 수행하였다. 연구는 상온과 고온다습 조건에서 적층과 형상을 변수로 실험적으로 수행되었다. 실험결과를 바탕으로 다음과 같은 결론을 얻었다. 하중-변위 선도는 두 가지 형태로 관찰되었으며, 각 파손 모드는 하중-변위 선도로 특징지어진다. 고온다습 조건의 파손형태는 베어링 파손 모드이며, 베어링 파손 모드에서 파손 강도는 유효강성의 영향이 크지 않다고 분석된다. 고온다습 조건의 파손강도 감소는 침투한 수분에 의해 섬유와 모재의 층간 결합부의 물성 저하에 기인한다.

Keywords: carbon fiber reinforced polymeric composites, two serial, elevated temperature wet,failure strength

Keywords: 탄소섬유강화 복합재료, 2열 볼트 체결 복합재 조인트, 고온다습, 파손강도