This study reviews previous research on various coating materials and methods designed to improve the adhesion and durability of steel pipes exposed to real-world marine environments, with the goal of identifying optimal solutions. The results concerning the adhesion and corrosion resistance of the pipes were categorized and analyzed based on exposure tests in extreme marine conditions to evaluate their stability. Furthermore, a detailed microstructural analysis of the coatings applied to the pipes was performed to assess surface damage, including peeling and delamination. The findings confirmed that coatings effectively prevent corrosion and provide sufficient adhesion and durability. Based on these results, we have proposed suitable coating materials, types, and application methods for steel pipes used in marine environments and offered recommendations for future exposure tests.

본 연구에서는 해양 환경 노출 강관에 적용되는 코팅의 부착 및 내구성 향상을 목표로, 코팅 재료 및 공법에 관한 기존 연구 결과를 바탕으로 최적의 코팅 재료와 공법을 선정하고자 하였다. 구체적으로, 서로 다른 코팅 종류와 공법이 적용된 해양 환경 노출 강관의 부착 및 내부식성 변화를 조사하고 분석하였다. 이후, 해양 환경에 노출된 코팅 재료의 미세 구조 분석 결과를 종합하여 표면 코팅의 탈락 및 손상 정도(peeling and delamination)를 평가하였다. 이를 통해 부착 성능과 내구성이 개선된 코팅을 적용할 경우, 해양 환경에 노출된 강관의 부식을 효과적으로 방지할 수 있음을 확인하였다. 분석 결과를 바탕으로 해양 환경에 적합한 강관 코팅 재료 유형 및 공법을 제시하였으며, 실해역 실험 수행 시 고려해야 할 요인과 현장 연구의 중요성을 강조하였다.

Keywords: 강관(Steel pipe), 코팅(Coating), 해양환경(Marine environment), 부식(Corrosion), 부착(Adhesion)