In the manufacturing process of thermosetting carbon fiber composite materials using an autoclave, the internal temperature changes according to the set temperature cycle. This temperature change causes the resin in the composite material to cure. Heat is generated through the chemical reaction of the resin, which can result in a difference between the temperature inside the autoclave and the temperature of the composite material. Previous research assumed that the temperatures of the composite material and the autoclave were the same and analyzed to predict the residual stress and thermal deformation after manufacturing. However, these stresses and deformations depend on the temperature and degree of cure of the composite material. Therefore, this study verifies a thermal-chemical model analysis technique that takes into account the heat generated by the chemical reaction of the resin to accurately calculate the temperature and degree of cure. Additionally, case studies were conducted for different thicknesses to investigate whether this model exhibits similar trends across varying thicknesses

오토클레이브를 사용하는 열경화성 탄소 섬유 복합재 성형 공정에서는 설정한 온도 사이클에 따라 내부 온도가 변화한다. 이 온도 변화에 따라 복합재 수지가 경화되며 성형이 진행된다. 이러한 과정에서 수지의 화학 반응으로 열이 발생하며, 이로 인해 오토클레이브 내부 온도와 복합재의 온도가 다를 수 있는 상황이 나타난다. 이전 연구에서는 복합재와 오토클레이브의 온도를 동일하게 가정하고, 성형 후에 발생하는 잔류 응력과 열 변형을 예측하였다. 그러나 잔류 응력과 열 변형은 복합재 온도와 경화도에 따라 영향을 받는 요소이기 때문에, 본 연구는 수지의 화학 반응열을 고려하여 정확한 온도와 경화도 변화를 계산하는 열화학 모델 해석 기법을 검증하였다. 또한, 이 모델이 다른 두께에서도 이와 같은 경향성을 나타내는지 확인하기 위해 두께별 케이스 연구를 하였다

Keywords: 복합재(Composite), 열화학(Thermo-chemical), 열전달(Heat transfer), 경화도(Degree of cure)