VaRTM(Vacuum assisted resin transfer molding) and VAP(Vacuum assisted process) processes are a type of RTM(Resin transfer molding) process, and are typical out-of-autoclave (OOA) processes that can manufacture large structures at low cost. In this paper, a resin filling test was conducted to compare the VaRTM and VAP processes, and the filling process and dimensional stability were compared. In addition, an analysis method to simulate the filling process was developed, and a dielectric sensor was used to detect the flow front of the resin, which was compared with the analysis results. From the resin filling test, the total filling time of the composite plate was measured to be 48 minutes for the VAP process and 145 minutes for the VaRTM process, and the filling time by the VAP process was reduced by about 67%. In addition, it was confirmed that the VAP process was superior to the VaRTM process in the thickness control ability and uniformity of the composite plate

VaRTM(Vacuum assisted resin transfer molding)과 VAP(Vacuum assisted process) 공정은 RTM(Resin transfer modling) 공정의 한 종류로서, 대형구조물을 저가에 제작할 수 있는 대표적인 탈 오토클레이브(OOA, Out of Autoclave) 공정이다. 본 논문에서는 VaRTM과 VAP 공정을 상호 비교하기 위하여 수지 충진시험을 진행하였으며, 충진과정과 치수 안정성 등을 상호 비교하였다. 또한, 충진과정을 모사할 수 있는 해석기법을 개발하였으며, 유전센서를 사용하여 수지의 유동선단을 검출하여 이를 해석결과와 상호 비교하였다. 수지 충진시험 결과, 복합재 평판의 총 충진시간은 VAP공정은 48분, VaRTM 공정은 145분으로 측정되어, VAP 공정에 의한 충진시간이 VaRTM 대비 약 67% 단축되었으며, VAP공정이 VaRTM 공정에 비해 복합재 평판의 두께조절능력과 균일도가 우수함을 확인하였다

Keywords: 진공수지이송성형법(VaRTM), VAP, 수지충진해석(Resin filling analysis), 유전기법(Dielectrometry)