A combination of a metallic mesh and an adhesive layer of metallic particle/epoxy composite was introduced as an intermediate layer to enhance the adhesion between cold-sprayed particles and fiber-reinforced composites (FRCs). Aluminum was considered for both the metallic particles in the adhesive and the metallic mesh. To predict the mechanical characteristics of the intermediate bond layer under a high strain rate, the properties of the adhesive layer needed to be calculated or measured. Therefore, in this study, the Al particle/epoxy adhesive was homogenized by using a rule of mixture. To verify the homogenization, the penetration depth, and the thickness decrease after the cold spray deposition from the undeformed surface, was monitored with FE analysis and compared with experimental observation. The comparison displayed that the penetration depth was comparable to the diameters of one cold spray particle, and thus the homogenization approach can be reasonable for the prediction of the stress level of particulate polymer composite interlayer under a high strain rate for cold spray processing.

저온 분사된 입자와 섬유강화 복합재료 사이의 접착력을 향상시키기 위해 금속 메쉬와 금속 입자/에폭시 접착제가 조합된 중간층이 도입되었다. 저온 분사 입자 및 금속 메쉬 그리고 금속 입자에는 모두 알루미늄을 활용하였다. 높은 변형률 속도에서 중간 층의 응력을 예측하기 위해서는 접착제 물성의 측정 또는 계산이 필요하다. 따라서, 본 연구에서는 금속 입자/에폭시 접착제의 물성을 계산하기 위해 혼합법칙(Rule of mixture)을 활용한 균질화 기법의 연구를 진행하였다. 균질화 기법의 검증을 위해 금속 메쉬/접착제로 구성된 중간층에 알루미늄 입자를 활용한 저온 분사를 진행하여, 실험으로 측정된 입자의 침투 깊이를 유한요소 해석에서 계산된 입자의 침투 깊이와 비교하였다. 시험과 해석에서 저온 분사 입자 혹은 중간층에 도입된 입자 하나 수준 크기의 침투 결과를 확인하였고, 이를 통해 높은 변형률 속도를 갖는 입자강화 복합재료 층의 물성 예측에 있어 균질화 기법이 적용될 수 있는 가능성을 확인하였다

Keywords: 저온 분사(Cold spray), 중간층(Intermediate layer), 입자강화 폴리머 복합재료(Particulate polymer composite), 균질화기법(Homogenization), 존슨-쿡 소성 모델(Johnson-Cook (J-C) plastic model)