Recently, as global environmental issues for sustainable development, such as carbon neutrality, have emerged, disposal methods of glass fiber composites, a material of existing wind turbines, have become a problem. To solve this problem, in this study, 30kW wind turbine blades were manufactured using flax fiber-based composites, which are eco-friendly natural fiber composites that can replace existing glass fiber composites, and their suitability was evaluated. First, mechanical strength tests were conducted to verify the feasibility of using eco-friendly natural flax fiber composites as a wind turbine blade material, and as a result, better strength were confirmed compared to previous studies on the properties of flax fiber composites. In addition, the suitability was confirmed through a static strength performance evaluation test to measure the static strength of the flax fiber composite blade using the manufactured 30kW class flax fiber composite blade.

최근 탄소 중립 등 지속 가능한 발전을 위한 지구환경 문제가 대두되면서 기존 풍력터빈의 소재인 유리섬유 복합재의 폐기 시 처리 방안이 문제가 되고 있다. 이를 해결하기 위해 본 연구에서는 기존의 유리섬유 복합재를 대체할 수 있는 친환경 복합재인 아마섬유 기반 복합재를 활용하여 30kW 풍력터빈 블레이드를 제조하고 적합성을 평가하였다. 먼저 친환경 천연 아마섬유 복합재의 풍력터빈 블레이드 소재로 활용 가능성을 검증하기 위해 기계적 강도 시험을 수행하였으며, 그 결과 선행 아마섬유 복합재 물성 연구 대비 좀 더 우수한 강도가 측정된 것을 확인하였다. 또한 제작된 30kW 급 아마섬유 복합재 블레이드를 활용하여 아마섬유 복합재 블레이드의 정적 강도를 측정하는 정적강도 성능평가 시험을 통하여 적합성을 확인하였다.

Keywords: 소형 풍력터빈(Small wind turbine), 천연섬유 복합재(Natural fiber composite), 아마섬유(Flax fiber), 기계적 물성(Mechanical property), 블레이드 구조 시험(Blade structural test)