Since natural fibers are highly flammable, it is not easy to make them flame retardant. In this study, a liquid flame retardant based on phytic acid, APTES, and Thiourea, which are flame retardant candidates derived from nature, was prepared and its performance was verified through flame retardant treatment and flame retardancy evaluation of bamboo fibers. When a liquid flame retardant is used, it is possible to treat a large amount of natural fibers with flame retardant treatment. Nine types of flame-retardant treated bamboo fibers were prepared according to the Taguchi design of experiment method. Thereafter, vertical burning test and microcalorimeter test were performed for flame retardancy evaluation, and the surface of natural fibers before and after flame-retardant treatment was compared using scanning electron microscope. The results show that phytic acid has a significant effect on improving the flame retardancy of natural fibers. Through microstructure analysis, it was assumed that the phytic acid helps flame retardant to uniformly adhere to the surface of natural fibers. If such research results are utilized, it is possible to make a large amount of natural fibers high flammability in an eco-friendly way, which is expected to be advantageous for the application of prototypes

천연섬유는 가연성이 높아 난연화가 쉽지않으며, 친환경적인 특성을 활용하기 위해서는 친환경적으로 난연화시키는 것이 필요하다. 본 연구에서는 자연으로부터 유래한 난연 후보물질인 Phytic acid, APTES, Thiourea를 기반으로 하는 액상 난연제를 제조하고 대나무 섬유의 난연처리 및 난연성 평가를 통하여 그 성능을 입증하고자 하였다. 액상 난연제를 사용할 경우 대량의 천연섬유에 대한 난연처리가 가능하다. 다구찌 시험계획법에 따라 9종류의 난연처리된 대나무 섬유를 준비하였다. 그후 난연성 평가를 위하여 수직 연소시험 및 마이크로칼로리미터 시험을 수행하였으며, SEM을 이용하여 난연처리 전후의 천연섬유 표면을 비교하였다. 시험결과 Phytic acid가 천연섬유의 난연성 향상에 매우 큰 효과가 있음을 알 수 있었으며 미세구조 분석을 통하여 난연제가 천연섬유 표면에 균일하게 부착되는데 도움을 주는 것을 알 수 있었다. 이와 같은 연구성과를 활용할 경우 대량의 천연섬유를 친환경적인 방법으로 고난연화 하는 것이 가능하여 시제품 적용에 유리할 것으로 기대된다

Keywords: 액상 난연제(Liquid flame retardant), 난연성(Retardancy), 친환경(Eco-friendly), 대나무 섬유(Bamboo fiber), 천연섬유(Natural fiber)