In this study, we measure the initial electrical conductivity of SCF/rubber specimens and SCF/rubber specimens with nickel particles respectively. The corresponding electrical conductivity with compressive strain on the specimens is also measured. Through this experiment, we observed the effects of the volume fraction of carbon fiber, nickel particles and external strain on the electrical conductivity. Experiments show that even a small difference in the volume fraction of SCF plays a major role in the change of the electrical conductivity and that the piezoresistivity increases due to fiber reorientation respond to external strain. In addition, the nickel particles contribute to improving the electrical conductivity in specimens with carbon fibers above the threshold volume fraction. It was confirmed that there is an effect of offsetting the increment in the piezoresistivity caused by the reorientation of carbon fibers according to external strain.

본 연구에서는 탄소 단섬유를 천연고무 기지에 혼합한 탄소섬유/고무 시편과 그에 니켈입자를 추가한 탄소섬유-니켈입자/고무 시편의 초기 전기전도도를 측정하고, 그 시편에 압축스트레인을 가하면서 변화하는 전기전도도를 측정하였다. 실험을 통해 탄소섬유의 체적분율 및 추가된 니켈입자, 외부스트레인 등이 전기전도도에 미치는 영향을 관찰하였다. 탄소섬유 체적분율은 작은 차이로도 시편의 전기전도도의 변화에 매우 큰 역할을 하였고, 외부스트레인에 따른 탄소섬유 재배열에 의해 압저항이 증가하는 것을 알 수 있었다. 또한, 니켈입자의 추가는 탄소섬유가 임계체적분율 이상인 시편에서 전기전도도를 개선하는데 기여하는 것을 볼 수 있었는데, 이로부터 외부변형에 따른 탄소섬유의 재배열에 의해 압저항이 증가하는 현상을 상쇄하는 효과가 있음을 확인하였다.

Keywords: 압저항(Piezoresistivity), 퍼콜레이션 모델(Percolation model), 탄소 단섬유(Short carbon fiber, SCF), 탄소섬유-니켈입자/고무복합체(Carbon fiber-nickel powder/rubber matrix composite)