Over the past decade, liquid crystalline epoxy (LCER) has attracted much attention as a promising matrix for the development of efficient heat dissipation materials. This study presents a comprehensive study including synthesis, preparation and chacterization of polymer/inorganic composites using typical 4,4-diglycidyloxybiphenyl (DP) epoxy among LECR. To confirm the thermal conductivity of composite materials, we have prepared composite samples composed of epoxy resin and single-wall carbon nanotube (SWCNT) as a filler. In particular, DP composites exhibit higher thermal conductivity than commercial epoxy composites that use the same type of filler due to the highly ordered microstructure of the LCER. In addition, the thermal conductivity of the DP composite can be controlled by controlling the amount of filler. In particular, the DP composite containing a SWCNT content of 50 wt% has the highest thermal conductivity of 2.008 W/mK

지난 10년간 효율적인 방열 재료 개발을 위해 유망한 매트릭스로서 액정 에폭시 수지(Liquid crystalline epoxy, LCER)는 많은 주목을 받아 왔다. 본 연구에서는 LECR중에서 대표적인 4,4-diglycidyloxybiphenyl (DP) 에폭시를 이용한 고분자/SWCNT 복합체의 합성과 제조 및 특성 분석을 포함한 포괄적 인 연구를 제시한다. 복합 재료의 열전도 특성을 확인해보기 위해 에폭시 수지와 충전제인 단일벽 탄소나노튜브(Single-wall carbon nanotube, SWCNT)로 구성된 복합체 샘플이 준비되었다. 특히 DP 복합체는, LCER의 고도로 정렬 된 미세 구조로 인해 동일한 필러를 사용하는 상업용 에폭시의 복합체에 비해 높은 열 전도성을 보였다. 또한, DP 복합체의 열전도도는 충전제의 양을 조절하여 제어할 수 있으며, 특히 SWCNT의 함량이 50 wt%인 DP 복합체는 열전도도는 2.008 W/mK로 가장 높은 열전도도를 나타내었다

Keywords: 액정성 에폭시(Liquid crystalline epoxy), 열전도도(Thermal conductivity), 복합재료(Composite material), 단일벽 탄소나노튜브(Single wall carbon nanotube)