In this paper, a progressive failure analysis method was developed using the Hashin failure criterion and crack band model. Using the failure criterion, the failure initiation was evaluated. If the failure initiation is occurred, the damage variables at each failure modes (fiber tension & compression, matrix tension & compression) was calculated according to linear softening degradation behavior and the variables are used to derive the damaged stiffness matrix. The damaged stiffness matrix is reflected to damaged material and the progressive failure analysis is continued until the damage variables to be 1 that complete failure of material. A series of processes were performed using FE commercial code ABAQUS with user defined material subroutine (UMAT). To evaluate the proposed progressive failure model, the experimental results of open hole composite laminate tests was compared with numerical result. Using digital image correlation system, the strain behavior also was compared. The proposed numerical results were coincided well with the experimental results.

본 논문에서는 Hashin 파손 기준식과 crack band 모델이 접목된 손상변수를 이용하여 점진적파손해석 방법이 개발되었다. 파손기준식을 이용하여 파손의 개시 유무가 판단된다. 파손이 개시된 경우에는 각 파손모드(섬유 인장/압축, 기지 인장/압축)에서 손상변수가 선형 열화 거동에 따라 계산되고, 손상강성행렬을 계산하는데 사용된다. 손상강성행렬은 손상된 재료에 반영되고, 계산된 손상강성행렬을 이용하여 재료의 완전한 파괴를 의미하는 손상변수가 1인 시점이 되기까지 점진적 파손해석이 계속해서 반복적으로 수행된다. 일련의 과정들은 상용해석프로그램인 ABAQUS에 사용자 정의 부프로그램을 이용하여 수행되었다. 제안된 점진적파손해석 도구의 검증을 위하여, 원공을 가진 복합재료 적층판의 시험 결과와 비교를 수행하였으며, 시험 중 디지털 이미지 상관법을 이용하여 획득한 변형률 거동과 해석을 통해 획득한 변형률 거동을 비교하였다. 제안된 해석결과는 시험 결과와 비교하여 유효한 일치를 보였다.

Keywords: 복합재료(Composite materials), 점진적파손해석(Progressive failure analysis), 디지털이미지상관법(Digital image correlation), 손상변수(Damage variable)