  • A Study on the Mechanical Behavior of Biomimetic Fiber-Reinforced Composites under Pressure Loads
  • Jinho Lee, Hyun-Seok Jo, Myungsoo Kim
  • The Research Institute of Natural Science and Department of Physics Education, Gyeongsang National University,Department of Mechanical Design Engineering, Youngsan University,School of Automotive Engineering, Youngsan University
  • 압력하중 하에서 생체모방 섬유강화 복합재의 기계적 거동 연구
  • 이진호, 조현석, 김명수
Abstract
In this study, we investigated the effect of fiber alignment in helicoidal structure on the mechanical properties of biomimetic fiber-reinforced composites. Using finite element analysis, circular biomimetic fiber composites were designed and studied. Various amounts of pressure loads were applied to a surface of the composites, and then bending and failure behaviors of the composites were analyzed. The results showed various failure morphologies according to the orientation of the fibers, and it turned out that the fiber alignment in helicoidal structure significantly improved the bending strength of the composite under pressure loading. This was because the fiber alignment in various directions for each layer dispersed effectively the fracture energy from the external load into multiple directions.

본 연구에서는 생체모방 섬유강화 복합재에서 섬유의 나선형 구조의 배열이 복합재의 기계적 물성에 미 치는 영향을 연구하였다. 유한요소해석을 이용해 원형의 생체모방 섬유강화 복합재를 구성하였고, 다양한 크기의 압력하중을 복합재 면에 적용시켜 굽힘과 파괴 거동의 결과를 분석하였다. 섬유의 정렬 방향에 따라 파괴 형상이 다르게 나타났고, 복합재에서 섬유의 나선형 구조 배열이 압력하중하에서 복합재의 굽힘 파괴강도를 크게 향상시 키는 것으로 나타났다. 이는 섬유가 각 층별로 여러 방향으로 정렬되어 외부하중에 의한 파괴에너지가 여러방향 으로 분산되는 것에서 기인한다.

Keywords: Biomimetic composites, Fiber-reinforced composites, Helicoidal structure, Mechanical property