  • Effect of Various Sizing Agents on the Properties of Nylon6/Carbon Fiber Composites Prepared by Reactive Process
  • Park Ha-Neul, Lee Hak Sung, Huh Mongyoung
  • Composites Processing Division, Korea Institute of Carbon Convergence Technology, Jeonju 54853, Korea
  • 다양한 사이징제가 반응중합에 의해 제조된 나일론 6/탄소섬유 복합체의 물성에 미치는 영향
  • 박하늘, 이학성, 허몽영
Abstract
In order to improve the interfacial bonding force and reaction polymerization degree of the carbon fiber reinforced nylon 6 composite material, the surface of the existing epoxy-sizing carbon fiber was desized to remove the epoxy and treated with urethane, nylon and phenoxy sizing agent, was observed. The interfacial bond strength of the resized carbon fiber was confirmed by IFSS (Interfacial Shear Strength) and the fracture surface was observed by scanning electron microscope. The results showed that the interfacial bonding strength of the carbon fiber treated with nylon and phenoxy sizing agents was higher than that of urethane - based sizing. It has been found that the urethane - type resizing carbon fiber has lower interfacial bonding strength than the conventional epoxy - sizing carbon fiber. This result shows that the interfacial bonding between carbon fiber and nylon 6 is improved by removing low activity and smoothness of existing carbon fiber.

탄소섬유 강화 PA6 복합재료의 탄소섬유-메트릭스간 계면결합력과 반응중합도 향상을 위해서 기존 탄소섬유의 에폭시 사이징제를 디사이징처리하여 에폭시를 제거한 후 우레탄계, 나일론계, 페녹시계 사이징제로 재처리해주었으며, 리사이징 처리된 탄소섬유의 표면을 관찰하였다. 리사이징 처리된 탄소섬유의 계면 결합력은 IFSS(Interfacialshear strength)를 통해서 확인하였으며, 계면 결합 강도 측정 후 파단면은 주사전자현미경을 통해서 관찰하였다. 나일론계와 페녹시계 사이징제로 처리된 탄소섬유가 우레탄계 사이징에 비해 계면 결합력이 상승한 것을 확인하였다. 우레탄계 리사이징 처리된 탄소섬유는 기존 에폭시 사이징 탄소섬유보다 계면 결합력이 감소한 것으로 확인되었다. 이 결과는 기존 탄소섬유의 저활성과 평활성을 제거하여 탄소섬유와 나일론6 사이의 계면 결합력이 향상된 것으로 판단된다.

Keywords: Carbon fiber, Nylon6, Interfacial shear strength, Resizing treatment

Keywords: 탄소섬유, 나일론6, 계면결합강도, 리사이징처리