  • Thermal/Mechanical Properties of Hafnium Carbide Coatings on Carbon-Carbon Composites
  • So-dam Choi, Hyoung-IL Seo, Byung-Joo Lim, Ihn Cheol Sihn, Jung Min Lee, Jong Kyoo Park, Kee Sung Lee
  • Department of Mechanical Design, Kookmin University, School of Mechanical Engineering, Kookmin University, Corresponding author, Dae Yang Co., Agency for Defense Development
  • 탄소-탄소 복합재료의 하프늄 탄화물 코팅재의 열적/기계적 특성
  • 최소담, 서형일, 임병주, 신인철, 이정민, 박종규, 이기성
Abstract
This study investigates thermal and mechanical characterization of Hafnium carbide coating on the Cf-C composites. The hafnium carbide coatings by vacuum plasma spray on the C/C-SiC composites are prepared to evaluate oxidation and wear resistance. We perform the thermal durability tests by thermal cycling at 1200oC for 10cycles in air and investigates the weight change of each cycle. We also evaluate the wear and indentation behavior using tungsten carbide ball indenter as a mechanical evaluation. As a result, the HfC coating is beneficial to reduce of weight loss during thermal cycling test and improve the elastic property of C/C-SiC composite. Especially, the HfC coating improves the wear resistance of C/C-SiC composite.

본 논문에서는 C/C-SiC 복합재료의 하프늄 탄화물 코팅재에 대한 열적, 기계적 특성을 평가하였으며 특히 코팅에 의한 내산화성과 내마모성의 향상여부를 평가하였다. 하프늄 탄화물(HfC)을 용사시켜 코팅한 샘플들을 가공한 후, 공기 중에서 열적 특성평가 및 마모, 압입시험 평가에 대한 연구를 수행하였다. 공기 중에서 1200oC의 온도까지 승온시킨 후 1시간 유지하는 싸이클을 10싸이클 진행하여 각 싸이클마다의 무게변화를 통해 탄소의 산화저항성을 평가하였고, 초경 구(tungsten carbide)를 사용하여 마모시험과 압입시험을 수행하여 그 결과를 비교하였다. 열피로 시험 수행 결과 하프늄 탄화물 코팅재가 상대적으로 무게감소가 적어 상대적으로 내산화성이 높은 것으로 평가되었다. 코팅된 하프늄 탄화물에 의해 탄성계수가 상대적으로 증가하였으며, 또한 C/C-SiC 복합재료는 하프늄 탄화물의 코팅에 의하여 내마모성이 향상되어 동일조건에서 마모량이 상대적으로 적었고 낮고 안정된 마찰계수가 유지되었다.

Keywords: HfC coating, Oxidation resistance, Wear resistance, Indentation properties

Keywords: 하프늄코팅, 산화저항성, 마모저항성, 압입특성