The structural adhesive have been manufactured for improvement of bonding process between CFRP and metal. The optimal condition for bonding process were investigated by evaluating the lap shear strength with amount of adhesive and curing time and the surface treatment of the CFRP. To confirm proper adhesion conditions, the fracture sections between CFRP and metal was observed using reflection microscope. Not only the improvement of the adhesion condition was important, but surface treatment on CFRP was also important. The optimal curing temperature was at 180oC for 20 minutes. The improvement for adhesive property was confirmed After surface treatment on CFRP. The optimal amount of structural adhesive for bonding between CFRP and metal was 1.5 × 10-3 g/mm2. Through the optimization of bonding process, the improvement of mechanical property over 10% is confirmed in comparison with existing adhesive.

CFRP와 금속간의 접합공정이 개선된 구조용 접착제가 제조되었다. 구조용 접착제에 대한 경화시간, 기 지재료의 표면상태 그리고 접착제의 양에 따른 최적의 접합공정 조건을 랩쉐어 실험을 통하여 파악하였다. 적합 한 접합조건을 확인하기 위해 이종재료간의 접합 파단면 상태를 반사현미경을 이용하여 평가하였다. 이종재료간 접합력 향상을 위해 접착제의 개선뿐만 아니라 CFRP의 표면처리 또한 중요하였다. 구조용 접착제의 경우 180도 조건에 20분의 경화온도 조건이 최적이였으며, CFRP의 표면 처리에 따라 접합특성이 향상됨을 확인하였다. 이종 재료 간 접합을 위해 구조용 접착제의 양은 1.5 × 10-3 g/mm2 조건일 때 최적이었다. 접합공정의 개선 및 최적화를 통해 기존의 접착력 대비 10% 이상의 물성 강화를 나타냄을 확인하였다.

Keywords: Structural adhesive, Adhesion process, Adhesion properties, CFRP/metal dual material

Keywords: 구조용 접착제, 접합공정, 접착특성, 탄소섬 유강화 복합재료/금속 이종소재