  • Carbon Fiber/Aluminum Composite Fabrication Using Wettability Control
  • Yongbeom Lee*, Sangjin Park*, Jun Hyun Han*†
  • *†Dept. of Materials Science and Engineering, Chungnam National University, Daejeon 34134, Korea
  • 젖음성 제어를 이용한 탄소섬유/알루미늄 복합재료 제조
  • 이용범*, 박상진*, 한준현*†
Abstract
Carbon fiber/aluminum (CF/Al) composites were successfully fabricated without pressure casting using wettability modification of carbon fiber. The wettability of liquid aluminum on carbon fibers was enhanced through electroless plating of copper on carbon fibers. Liquid aluminum was well infiltrated into carbon fiber bundles with Cu coating layer due to low wetting angle, and a lot of pores that existed in CF/Al composite without Cu coating on CF were greatly removed. However, a few tiny pores existed in carbon fiber bundles, which is due to not bad wettability between CF and Al but shrinkage cavity that was generated during cooling of CF/Al composite. The tiny pores could be effectively removed by a subsequent rolling.

탄소섬유에 대한 액상 알루미늄의 젖음성이 매우 좋지 않기 때문에 통상적인 주조방법으로는 기공이 없 는 건전한 탄소섬유/알루미늄 복합재료 제조가 어려워 이를 극복하기 위해서는 복합재료 주조 시 고온, 고압이 요 구된다. 본 연구에서는 탄소섬유 표면에 무전해 도금에 의해 구리를 코팅함으로써 탄소섬유에 대한 알루미늄의 젖음성을 향상시켜 고온, 고압을 가하지 않고 액상의 알루미늄이 탄소섬유들 사이를 자발적으로 침투하여 내부 기공이 매우 적은 건전한 탄소섬유/알루미늄 복합재료를 제조할 수 있었다. 제조된 탄소섬유/알루미늄 복합재료 내 일부 탄소섬유 다발 안에서 미세기공이 발생하였으나 이 미세기공은 압연과 같은 후 가공에 의해 탄소섬유와 알루미늄 사이의 계면분리나 탄소섬유의 파괴 없이 효과적으로 제거될 수 있었다. 복합재료 제조 시 발생한 미세 기공은 탄소섬유와 알루미늄의 젖음성 문제는 아니며 탄소섬유들 사이 공간을 효과적으로 채웠던 액상 알루미늄 이 냉각되는 동안 수축으로 인해 일부 탄소섬유들 사이로부터 빠져 나가 수축공 형태의 기공이 발생한 것으로 판단된다.

Keywords: Carbon fiber, Composite materials, Aluminum, Wettability

Keywords: 탄소섬유, 복합재료, 알루미늄, 젖음성